For Stainless Stee |
|
Brand Name
|
Type of covering
|
Equivalent Specification
|
Welding Position
|
Type of Current
|
Chemical Composition of Deposited Wire(%)
|
Hardness
Properties of Deposited Metal
|
Applications
|
|
C
|
Mn
|
Si
|
S
|
P
|
Cr
|
Ni
|
Mo
|
Cu
|
Other
|
T.S.(MPa)
|
EL(%)
L=5D
|
|
CHK202
|
Lime titanium
|
WAS E410-16
JIS D410-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.12
|
<=1.00
|
<=0.90
|
<=0.030
|
<=0.040
|
11.0-13.5
|
<=0.70
|
<=0.75
|
<=0.75
|
- |
>=450
|
>=20
|
Welding of 0Cr13
stainless steels and similar steels, also surfacing for resistance to
corrosion and abrasion.
|
|
CHK207
|
Low hydrogen
sodium
|
WAS E410-15
GB E410-15
|
F, V,
OH, H
|
DC+
|
<=0.12
|
<=1.00
|
<=0.90
|
<=0.030
|
<=0.040
|
11.0-13.5
|
<=0.70
|
<=0.75
|
<=0.75
|
- |
>=450
|
>=20
|
Welding of 0Cr13
stainless steels and similar steels, also surfacing for resistance to
corrosion and abrasion.
|
|
CHK232
|
Lime
|
WAS
E410NiMo-16
GB E410NiMo-16
|
F, V,
OH, H
|
AC or DC+
|
0618
|
0.40-0.70
|
<=0.90
|
<=0.030
|
<=0.040
|
11.0-12.5
|
4.0-5.0
|
0.40-0.70
|
<=0.75
|
- |
>=760
|
>=15
|
Welding of 0Cr13
stainless steels and similar stainless steels, also surfacing for
resistance to corrosion and abrasion.
|
|
CHK307
|
Low hydrogen
sodium
|
WAS E430-15
GB E430-15
|
F, V,
OH, H
|
DC+
|
<=0.10
|
<=1.00
|
<=0.90
|
<=0.030
|
<=0.040
|
15.0-18.0
|
<=0.60
|
<=0.75
|
<=0.75
|
- |
>=450
|
>=20
|
Welding of Cr17
stainless steels structures of resistance to nitric acid corrosion and
heat.
|
|
CHS002
|
Extra low carbon
Lime titanium
|
WAS E308L-16
JIS D308L-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.04
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
18.0-21.0
|
9.00-11.00
|
<=0.75
|
<=0.75
|
- |
>=520
|
>=35
|
Welding of extra-low
carbon 00Cr21Ni10 stainless steels.
|
|
CHS002A
|
Extra low carbon
Lime titanium
|
WAS E308L-15
GB E308L-15
|
F, V,
OH, H
|
DC+
|
<=0.04
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
18.0-21.0
|
9.00-11.00
|
<=0.75
|
<=0.75
|
- |
>=520
|
>=35
|
Welding of extra-low
carbon 00Cr19Ni10 stainless steels.
|
|
CHS012Si
|
Lime titanium
|
- |
F, V,
OH, H
|
AC or DC+
|
<=0.04
|
<=1.00
|
3.50-4.30
|
<=0.030
|
<=0.035
|
18.0-22.0
|
12.0-15.0
|
0.20-0.50
|
-
|
- |
>=540
|
>=25
|
Welding of extra-low
carbon 00Cr17Ni155Si4Mo stainless steels of resistance to dense nitric
acid corrosion.
|
|
CHS022
|
Extra low carbon
Lime titanium
|
WAS E316L-16
JIS D316L-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.04
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
17.0-20.0
|
11.0-14.0
|
2.00-3.00
|
<=0.75
|
- |
>=490
|
>=30
|
Welding ofA1S1316,
316L used in petrochemical, chemical, textile and paper industries.
|
|
CHS122N
|
Extra low carbon
Lime titanium
|
WAS E316L-16
GB E316L-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.04
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
17.0-20.0
|
11.0-14.0
|
2.00-3.00
|
<=0.75
|
N
0.10
|
>=490
|
>=30
|
Welding of 316LN
stainless steels structures in the same system.
|
|
CHS022Si
|
Lime
|
- |
F, V,
OH, H
|
AC or DC+
|
<=0.05
|
<=0.08
|
<=0.60
|
<=0.030
|
<=0.035
|
18.50-20-50
|
10.50-12.50
|
2.00-3.00
|
-
|
- |
>=540
|
>=25
|
Welding of 3RE60
liner sheets or pipe structures, such as smelting equipments.
|
|
CHS032
|
Extra low carbon
Lime titanium
|
WAS
E316CuL-16
GB E316CuL-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.04
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.035
|
18.0-21.0
|
12.0-14.0
|
2.00-2.50
|
<=2.0
|
- |
>=540
|
>=25
|
Welding of the
stainless steels in the same system.
|
|
CHS042
|
Extra low carbon
Lime titanium
|
WAS
E309MoL-16
JIS D309MoL-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.04
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
22.0-25.0
|
12.0-14.0
|
2.00-3.00
|
<=0.75
|
- |
>=540
|
>=25
|
Welding of the
corresponding heat-resisting steels.
|
|
CHS052
|
Extra low carbon
Lime titanium
|
-
|
F, V,
OH, H
|
AC or DC+
|
<=0.04
|
<=2.00
|
<=0.90
|
<=0.030
|
<=0.035
|
17.3-20.0
|
22.0-25.0
|
4.00-5.50
|
-
|
- |
>=540
|
>=25
|
Welding of
00Cr18Ni24Mo5 marine corrosion resisting steels, chemical reactor of
resistance to sulphuric acid corrosion, welding of different stainless
steels.
|
|
CHS052Cu
|
Extra low carbon
Lime titanium
|
-
|
F, V,
OH, H
|
AC or DC+
|
<=0.04
|
<=2.00
|
<=1.00
|
<=0.030
|
<=0.035
|
17.0-22.0
|
22.0-27.0
|
4.00-5.50
|
1.00-2.00
|
- |
>=490
|
>=25
|
Welding of chemical reactor
and separator of resistance to sulphuric acid corrosion, acetic acid
corrosion and phosphoric acid corrosion.
|
|
CHS062
|
Extra low carbon
Lime titanium
|
WAS E309L-16
JIS D309L-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.04
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
22.0-25.0
|
12.0-14.0
|
<=0.75
|
<=0.75
|
- |
>=520
|
>=25
|
Welding of the
stainless steels to carbon and low alloy steels, such as synthetic fiber, petrochemical
equipment and nuclear reactor.
|
|
CHS062A
|
Extra low carbon
Lime titanium
|
WAS E309L-15
JIS D309L-15
|
F, V,
OH, H
|
DC+
|
<=0.04
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.035
|
22.0-25.0
|
12.0-14.0
|
<=0.75
|
<=0.75
|
- |
>=520
|
>=25
|
Welding of the
stainless steels to carbon and low alloy steels, such as synthetic fiber, petrochemical
equipment and nuclear reactor.
|
|
CHS102
|
Lime
|
WAS E308-16
JIS D308-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
18.0-21.0
|
9.0-1.0
|
<=0.75
|
<=0.75
|
- |
>=550
|
>=35
|
Welding of 0Cr18Ni9
and Cr18Ni9Ti stainless steels and working temperature is below 300oC.
|
|
CHS102Fe
|
Lime
|
WAS E308-16
GB E308-16
|
F, HF
|
AC or DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
18.0-21.0
|
9.0-11.0
|
<=0.75
|
<=0.75
|
- |
>=550
|
>=35
|
Welding of 0Cr18Ni9
stainless steels and working temperature is below 300oC.
|
|
CHS107
|
Low hydrogen
sodium
|
WAS E308-15
GB E308-15
|
F, V,
OH, H
|
DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
18.0-21.0
|
9.0-11.0
|
<=0.75
|
<=0.75
|
- |
>=550
|
>=35
|
Welding of 0Cr18Ni9
stainless steels and working temperature is below 300oC.
|
|
CHS122
|
Lime
|
-
|
F, V,
OH, H
|
AC or DC+
|
<=0.08
|
<=2.50
|
<=1.50
|
<=0.030
|
<=0.035
|
20.0-24.0
|
7.0-10.0
|
-
|
-
|
-
|
>=540
|
>=25
|
Welding of 0Cr18Ni9
crack resisting and corrosion stainless steel structures.
|
|
CHS132
|
Lime
|
WAS E347-16
JIS D347-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
18.0-21.0
|
9.0-11.00
|
<=0.75
|
<=0.75
|
Nb
8 x C% - 1.0
|
>=520
|
>=25
|
Suitable for welding
important resisting corrosion structures made of 1Cr18Ni9Ti stainless
steel that contents titanium stably.
|
|
CHS132Fe
|
Lime
|
WAS E347-16
GB E347-16
|
F, HF
|
AC or DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
18.0-21.0
|
9.0-11.00
|
<=0.75
|
<=0.75
|
Nb
8 x C% - 1.0
|
>=520
|
>=25
|
Welding of corrosion
resisting stainless steel and surfacing of carbon steels.
|
|
CHS137
|
Low hydrogen
sodium
|
WAS E347-15
GB E347-15
|
F, V,
OH, H
|
DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
18.0-21.0
|
9.0-11.00
|
<=0.75
|
<=0.75
|
Nb
8 x C% - 1.0
|
>=520
|
>=25
|
Welding of important
Cr18Ni9, 1Cr18Ni9Ti corrosion resisting stainless steel.
|
|
CHS157Mn
|
Low hydrogen
sodium
|
-
|
F, V,
OH, H
|
DC+
|
<=0.10
|
6.00-9.00
|
<=0.70
|
<=0.030
|
<=0.035
|
18.0-22.0
|
9.0-11.00
|
-
|
-
|
-
|
>=540
|
>=30
|
Welding of high
strength steels and different steels such as H157 steel.I.V.(J)20oC>=90.
|
|
CHS202
|
Lime
|
WAS E316-16
JIS D316-16
|
F, V,
OH, H
|
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
17.0-20.0
|
11.0-14.0
|
2.00-3.00
|
<=0.75
|
-
|
>=520
|
>=30
|
Welding of 18% Cr,
12% Ni, 2% Mo stainless steels and 13% Cr,17% Cr stainless steels.
|
|
CHS207
|
Low hydrogen
sodium
|
WAS E316-15
GB E316-15
|
F, V,
OH, H
|
DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
17.0-20.0
|
11.0-14.0
|
2.00-3.00
|
<=0.75
|
-
|
>=520
|
>=30
|
Welding of 18% Cr,
12% Ni, 2% Mo stainless steels and 13% Cr,17% Cr stainless steels.
|
|
CHS212
|
Lime
|
WAS E318-16
JIS D318-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
17.0-20.0
|
11.0-14.0
|
2.00-3.00
|
<=0.75
|
Nb
6 x C% - 1.0
|
>=550
|
>=25
|
Welding of important
Cr18Ni12MoTi and extra-low Cr18Ni12Mo2.
|
|
CHS222
|
Lime
|
WAS E316Cu-16
GB E316Cu-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.035
|
18.0-21.0
|
12.0-14.0
|
2.00-2.50
|
<=2.00
|
-
|
>=540
|
>=25
|
Welding of stainless
steel structures in the same system, which contains copper.
|
|
CHS232
|
Lime
|
GB
E0-18-12-Mo2V-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.035
|
17.0-20.0
|
11.0-14.0
|
2.00-2.50
|
<=0.50
|
V
0.30-0.70
|
>=540
|
>=25
|
Welding of Cr18Ni9Ti
and Cr18Ni12Mo2Ti normal heat resisting and certain corrosion resisting
stainless steel structure.
|
|
CHS237
|
Low hydrogen
sodium
|
GB
E0-18-12-Mo2V-15
|
F, V,
OH, H
|
DC+
|
<=0.08
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.035
|
17.0-20.0
|
11.0-14.0
|
2.00-2.50
|
<=0.50
|
V
0.30-0.70
|
>=540
|
>=25
|
Multi-layer welding
of Cr18Ni10Ti and Cr18Ni12Mo2Ti normal heat certain corrosion resisting
stainless steel structure.
|
|
CHS302
|
Lime
|
WAS E309-16
JIS D309-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.15
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
22.0-25.0
|
12.0-14.0
|
<=0.75
|
<=0.75
|
-
|
>=550
|
>=25
|
Welding of stainless
steel structures in the same system, different steels and high chromium
steels and high manganese steels etc.
|
|
CHS307
|
Low hydrogen
sodium
|
WAS E309-15
GB E309-15
|
F, V,
OH, H
|
DC+
|
<=0.15
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
22.0-25.0
|
12.0-14.0
|
<=0.75
|
<=0.75
|
-
|
>=550
|
>=25
|
Welding of stainless
steel structures in the same system, different steels and high chromium
steels and high manganese steels etc.
|
|
CHS312
|
Lime
|
WAS E309Mo-16
JIS D309Mo-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.12
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
22.0-25.0
|
12.0-14.0
|
2.00-3.00
|
<=0.75
|
-
|
>=550
|
>=25
|
Welding of stainless
steel structures in the same system which contains Mo.
|
|
CHS402
|
Lime
|
WAS E310-16
JIS D310-16
|
F, V,
OH, H
|
AC or DC+
|
0.08-0.20
|
1.00-2.50
|
<=0.75
|
<=0.030
|
<=0.030
|
25.0-28.0
|
20.0-22.5
|
<=0.75
|
<=0.75
|
-
|
>=550
|
>=25
|
Welding of heat
resisting stainless steel structures in the same system, lining of
stainless steels, also welding of high harden ability steel structures
such as Cr5Mo, Cr9Mo, Cr13 and Cr18, or welding between different seel.
|
|
CHS407
|
Low hydrogen
sodium
|
WAS E310-15
GB E310-15
|
F, V,
OH, H
|
DC+
|
0.08-0.20
|
1.00-2.50
|
<=0.75
|
<=0.030
|
<=0.030
|
25.0-28.0
|
20.0-22.5
|
<=0.75
|
<=0.75
|
-
|
>=550
|
>=25
|
Welding of heat
resisting stainless steel structures in the same system, lining of
stainless steels, also welding of high harden ability steel structures
such as Cr5Mo, Cr9Mo, Cr13 and Cr18, or welding between different seel.
|
|
CHS412
|
Lime
|
WAS E316Mo-16
GB E316Mo-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.12
|
1.00-2.50
|
<=0.75
|
<=0.030
|
<=0.030
|
25.0-28.0
|
20.0-22.0
|
2.00-3.00
|
<=0.75
|
-
|
>=550
|
>=25
|
Welding of heat
resisting stainless steels and different steels.
|
|
CHS437
|
Low hydrogen
sodium
|
WAS E310H-15
BS 25.20.H.B
|
F, V,
OH, H
|
DC+
|
0.25-0.45
|
5.00-8.00
|
<=0.60
|
<=0.030
|
<=0.030
|
23.0-26.0
|
18.0-21.0
|
-
|
-
|
-
|
>=540
|
>=22
|
Welding of HK40 high
temperature pipe and bottom roller of furnace.
|
|
CHS502
|
Lime
|
GB
E1-16-25Mo6N-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.12
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.035
|
14.0-18.0
|
22.0-27.0
|
5.00-7.00
|
<=0.50
|
N
>=0.10
|
>=420
|
>=30
|
Welding of quenched
low alloy steels, medium alloy steels, different steels, steels structures
which are required for higher rigidity and similar heat-resisting high strength
steels.
|
|
CHS507
|
Low hydrogen
sodium
|
GB
E1-16-25Mo6N-15
|
F, V,
OH, H
|
DC+
|
<=0.12
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.035
|
14.0-18.0
|
22.0-27.0
|
5.00-7.00
|
<=0.50
|
N
>=0.10
|
>=420
|
>=30
|
Welding of quenched
low alloy steels, medium alloy steels, different steels, steels structures
which are required for higher rigidity and similar heat-resisting high strength
steels.
|
|
CHS29.9
|
Lime
|
WAS E312-16
JIS D312-16
|
F, V,
OH, H
|
C or DC+
|
<=0.15
|
0.50-2.50
|
<=0.90
|
<=0.030
|
<=0.040
|
28.0-32.0
|
8.0-10.5
|
<=0.75
|
<=0.75
|
-
|
>=660
|
>=22
|
Welding of high
carbon steels, tool steels and different metals.
|
|
CHS29.9Co
|
Lime
|
WAS E312-16
GB E312-16
|
F, V,
OH, H
|
AC or DC+
|
<=0.15
0.09
|
0.50-2.50
0.20
|
<=1.30
1.0
|
<=0.30
0.015
|
<=0.040
0.020
|
26.0-29.0
27.5
|
8.0-12.0
10.5
|
-
|
-
|
Co
<=0.50
|
>=660
|
>=22
|
Welding of high
carbon steels, high alloy steels, tool steels, spring steels, Mn alloy
steels, hardening of surface steels, cast steels and high rapid steels.
Also welding of different steel structures between aforementioned steels.
|
|
CHS2209
|
Extra low carbon
Lime titanium
|
WAS E2209-16
GB E2209-16
|
F, V,
OH, H
|
AC or DC+
|
0415
|
0.50-2.00
|
<=0.90
|
<=0.030
|
<=0.040
|
21.5-23.5
|
8.5-10.5
|
2.5-3.5
|
<=0.75
|
-
|
>=690
|
>=20
|
Welding of extra low
carbon stainless steel structures such as petrochemical, hydraulic
projects.
|
|
|
|