CHF103/CHW-S2
Flux/Wire Combination for Submerged Arc Welding |
AWS F6A4-EM12
GB/T F4A4-H08MnA |
| |
|
|
Description:
CHF103/CHW-S2 flux/wire
combination has good performance in welding. The weld metal shows a fine
appearance and the deposited metal has a satisfactory low temperature
toughness and high crack resistance. Both AC and DC can be applied, when DC,
the wire should be contacted straight polarity. It is suitable to weld
450MPa-500MPa grade structures, such as boilers, bridges, pressure vessels,
as well as LPG cylinders. Before welding, the base metal must clear away
impurities and the flux must be baked in a temperature of 300℃-350℃ for 1.5-2 hours.
|
|
| Chemical Composition (Typical, %) |
|
C |
Mn |
Si |
S |
P |
Cr |
Ni |
Cu |
CHW-S2 (EM12)
(Standard) |
≤0.10 |
0.80-1.10 |
≤0.07 |
≤0.030 |
≤0.030 |
≤0.20 |
≤0.30 |
≤0.20 |
CHW-S2 (EM12)
(Typical) |
0.070 |
0.95 |
0.03 |
0.018 |
0.011 |
0.02 |
0.02 |
0.009 |
Deposited Metal
(Typical) |
0.065 |
1.00 |
0.26 |
0.010 |
0.016 |
0.02 |
0.02 |
0.12 |
|
Mechanical Properties of Deposited Metal |
|
Yield Point
(бs,
MPa) |
Tensile Strength
(бb,
MPa) |
Elongation
(δ5,
%) |
Impact Value (J) |
0℃ |
Standard |
≥330 |
415-550 |
≥22 |
≥27 |
Typical |
360 |
470 |
30 |
100 |
|
|