Atlantic Welding Consumables
 

Flux Cored Wire
Flux Cored Wire  药芯焊丝
Item Code Equivalent Norm Welding Position Standard & Typical Chemical Composition of Deposited Metal (%)       Standard & Typical Mechanical Properties of Deposited Metal Applications
C Mn Si S P Cr Ni Mo V Yield Point       ReL (MPa) Tensile Strength   
Rm (MPa) 		Elongation    
A (%) 		Akv Value (J) Shield Gas
Temp.(℃) Joule
CHT611 AWS A5.20 E61T-GC F,VD,   OH,H — ≤1.75 ≤0.90 ≤0.03 ≤0.03 — — — — ≥330 ≥415 ≥22 0 ≥47  120 CO2  Suitable for all position as well as vertical down welding for mild steels.  
0.055 0.90 0.30 0.008 0.02 — — — — 430 505 29 -20 100
CHT701 AWS A5.20 E70T-1C F,HF ≤0.10 ≤1.75 ≤0.75 ≤0.03 ≤0.03 — — — — ≥400 ≥480 ≥22 -20 ≥27  70 CO2  It is suitable for flat or horizontal filler of thick or medial thick mild
steel structures fabricated by 490MPa grade high tensile steels.  		 
0.06 1.40 0.45 0.011 0.018 — — — — 450 545 29
CHT70B AWS A5.20 E70T-5C F,HF,V ≤0.12 ≤1.75 ≤0.90 ≤0.03 ≤0.03 — — — — ≥400 490-670 ≥22 -30 ≥27
150 		CO2  It is suitable for flat or horizontal filler of higher tensile, better crack- resisting mild steel structures fabricated by 490MPa grade high strength steels. Also it could be vertical up welding on which angle below 45°.  
0.07 1.50 0.50 0.013 0.018 — — — — 435 545 28
CHT711 AWS A5.20 E71T-1C F,V,   OH,H ≤0.12 ≤1.75 ≤0.90 ≤0.03 ≤0.03 — — — — ≥400 490-670 ≥22 0 ≥47  120 CO2  It is widely used in structures fabricated by mild steel and 490MPa grade high tensile steel, such as ships, pressure vessels, machineries, bridges, etc. CCS,LR,ABS,BV,GL,DNV, NK,BKI,CWB
0.055 1.35 0.40 0.009 0.018 — — — — 440 535 32 -20 ≥27  100
CHT71Ni AWS A5.20 E71T1-1C-J F,V,   OH,H ≤0.10 ≤1.75 ≤0.90 ≤0.03 ≤0.03 — ≤0.5 — — ≥400 490-670 ≥22 -40 ≥27
80 		CO2  Suitable for structures fabricated by mild steel or 490MPa grade high tensile
steels, such as pressure vessels, offshore drilling platforms, pipelines, etc.  		 
0.055 1.30 0.35 0.015 0.02 — 0.45 — — 425 520 30
CHT80B2B AWS A5.29 E80T5-B2C F,HF,V ≤0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 1.0-1.5 — 0.4-0.65 — ≥470 550-690 ≥19 20 ≥47
180 		CO2  It is suitable for flat, horizontal filler or vertical up welding on which angle below 45°, higher tensile, better crack-resisting structures that fabricated by 550MPa grade heat resistant low alloy steels, which work temperature lower than 520℃.Welded piece should be preheated to 150-300℃ and after welding it should be tempered in 680-720℃.  
0.053 0.92 0.40 0.01 0.012 1.15 — 0.45 — 510 600 24
CHT81B2 AWS A5.29 E81T1-B2C F,V,   OH,H ≤0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 1.0-1.5 — 0.4-0.65 — ≥470 550-690 ≥19 20 ≥27
75 		CO2  Suitable for welding 550MPa grade heat resistant low alloy steel structures,which work temperature lower than 520℃, e.g.15CrMo (1%Cr-0.5%Mo). Welded piece should be preheated to 150-300℃ and after welding it should be tempered in 680-720℃.  
0.058 0.90 0.40 0.01 0.011 1.15 — 0.45 — 550 630 23
CHT81B2V DGS K1801.01-2006 F,V,
OH,H 		≤0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 1.0-1.5 — 0.4-0.65 0.1-0.35 ≥470 ≥550 ≥19 20 ≥27
70 		CO2  Suitable for welding 550MPa grade heat resistant low alloy pearlitic steel
structures, which work temperature below 540℃, e.g.12Cr1MoV. Welded piece should be preheated to 150-300℃ and after welding it should be tempered in 700-740℃. 		 
0.055 0.90 0.40 0.01 0.011 1.15 — 0.45 0.15 540 640 22
CHT81K2 AWS A5.29 E81T1-K2C F,V,
OH,H 		≤0.15 0.5-1.75 ≤0.80 ≤0.03 ≤0.03 ≤0.15 1.0-2.0 — ≤0.05 ≥470 550-690 ≥19 -30 ≥27
111 		CO2  It is used in structures fabricated by 550MPa grade high tensile steel, such as ships, pressure vessels, machineries, bridges, offshore drilling platforms, etc.  
0.05 1.35 0.35 0.008 0.017 0.02 1.45 — 0.014 495 580 28  
CHT81Ni2 AWS A5.29 E81T1-Ni2C F,V,
OH,H 		≤0.12 ≤1.50 ≤0.80 ≤0.03 ≤0.03 — 1.75-2.75 — — ≥470 550-690 ≥19 -40 ≥27
90 		CO2  It is used in structures fabricated by 550MPa grade high tensile steel, such as ships, pressure vessels, machineries, bridges, offshore drilling platforms, etc.  
0.05 1.10 0.35 0.008 0.017 — 2.20 — — 485 580 28  
CHT90B3B AWS  A5.29  E91T5-B3C F,HF,V ≤0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 2.0-2.5 — 0.90-1.20 — ≥540 620-760 ≥17 20 ≥27
150 		CO2  Suitable for welding 600MPa grade 25%Cr-1%Mo heat resistant low alloy steel structures, which work temperature below 550℃, such as high temperature, high pressure pipes, chemical machineary, petroleum thermal cracking equirments, etc. Welded piece should be preheated to 150-300℃ and after welding it should be tempered in 680-720℃.    
0.068 1.01 0.35 0.01 0.018 2.15 — 1.08 — 565 660 21
CHT91B3 AWS  A5.29  E91T1-B3C F,V,
OH,H 		≤0.12 ≤1.25 ≤0.80 ≤0.03 ≤0.03 2.0-2.5 — 0.90-1.20 — ≥540 620-760 ≥17 20 ≥27
60 		CO2  Suitable for welding 600MPa grade 25%Cr-1%Mo heat resistant low alloy steel structures, which work temperature below 550℃, such as high temperature, high pressure pipes, chemical machineary, petroleum thermal cracking equirments, etc. Welded piece should be preheated to 150-300℃ and after welding it should be tempered in 680-720℃.   
0.06 1.10 0.47 0.012 0.018 2.26 — 1.06 — 600 730 20
CHT91K2 AWS  A5.29  E91T1-K2C F,V,
OH,H 		≤0.15 0.5-1.75 ≤0.80 ≤0.03 ≤0.03 ≤0.15 1.0-2.0 ≤0.35 ≤0.05 ≥540 620-760 ≥17 -20 ≥27
70 		CO2  Suitable for welding structures fabricated by 600MPa grade high tensile  steel, such as ships, pressure vessels, machineries, petroleum & chemical industries, bridges etc.    
0.05 1.45 0.40 0.013 0.018 0.022 1.55 0.13 0.012 560 650 23