CHF101GX/CHW-SG
Flux/Wire Combination for Submerged Arc Welding
AWS F7A4-EG-G
Description: CHF101GX/CHW-SGflux/wire
combination has excellence welding performance. The weld metal shows a fine
appearance and the deposited metal has a satisfactory low temperature
toughness and high crack resistance. Both AC and DC can be applied, when DC,
the wire should be contacted straight polarity. It is used to weld 500MPa
important high strength steel structures, especially for Spiral or
longitudinal welded huge diameter pipe made by X65 & X70 steels. It could be
four wires welding and the welding speed is 1.70m-2.00m per minute. Before
welding, the base metal must clear away impurities and the flux must be
baked in a temperature of 350℃ for 2 hours.
Chemical Composition (Typical, %)
C
Mn
Si
S
P
Ni
Cr
Ti
Cu
CHW-SG (EG)
0.068
1.37
0.07
0.008
0.018
0.28
0.01
0.06
0.10
Deposited Metal
0.049
1.42
0.35
0.005
0.018
0.29
0.008
0.01
0.08
Mechanical Properties of Deposited Metal
Yield Point
(бs,
MPa)
Tensile Strength
(бb,
MPa)
Elongation
(δ5, %)
Impact Value (J)
-40℃
Standard
≥400
480-650
≥22
≥27
Typical
490
580
28
110
Mechanical Properties of
Deposited Metal of Welded Joint