CHE501Fe18
Iron Power Electrode for Welding Mild Steel
or High Tensile Steel
AWS
A5.1 E7024
BS EN ISO 2560-B-E 49 24 -1 A
GB/T 5117 E5024
JIS Z3212 D5000
Description: CHE501Fe18 is a high deposition
rate iron powder titania type welding rod for mild steel or high tensile
steel giving a metal recovery of about 180%. It is suitable for welding
structures fabricated by H-beams or T-beams, as well as flat and horizontal
fillet welding medium and thick plate. The rods should be baked for 1 hour
at the temperature of 150℃ before welding.
Chemical
Composition of Deposited Metal(%)
C
Mn
Si
S
P
Cr*
Ni*
Mo*
V*
Standard
≤0.15
≤1.25
≤0.90
≤0.035
≤0.035
≤0.20
≤0.30
≤0.30
≤0.08
Typical
0.068
0.74
0.44
0.015
0.024
0.027
0.006
0.003
0.016
The total
amount of elements with*one should be ≤1.50%
Mechanical Properties of Deposited Metal
Yield Point
ReH (MPa)
Tensile Strength
Rm (MPa)
Elongation
A4
(%)
Impact Value (J)
0℃
Standard
≥375
490-660
≥22
≥47
Typical
450
510
27
72
Sizes, Pieces & Recommended Current Range
(AC or DC+)