Solid Wire for MIG Welding

   
Solid Wire for MIG Welding   惰性气体保护焊实芯焊丝                        
Item Code Equivalent Norm Chemical Composition of Wire (%, Typical) Mechanical Properties of Deposited Metal (Typical) Application
C Mn Si S P Cr Ni Mo Cu Others Yield Point
Rp02 (MPa)		 Tensile Strength
Rm (MPa)		 Elongation            A4 (%) Akv Value (J) Shield Gas
CHM-307Si AWS A5.9 ER307Si                             BS EN ISO  14343-A-G 18 8 Mn 0.077 6.88 0.77 0.01 0.02 19.12 8.57 0.04 0.16 — — 605 42.5  25℃   100  97Ar+3%O2 Suitable for welding structures fabricated by high tensile strength steels and dissimilar steels, e.g.armor plate, H617 steel, etc.
CHM-308 AWS A5.9 ER308                                BS EN ISO  14343-B-SS308                 JIS Z3321 Y308 0.05 1.79 0.48 ### 0.022 #### 9.40 0.008 0.09 — — 580 42 — 98%Ar+2%O2 For Cr18Ni8, Cr18Ni12, Cr20Ni10 austenitic stainless steels, such as 301 ,302 & 308, etc. especially 304.
CHM-308L AWS A5.9 ER308L                              BS EN ISO  14343-A-G（19 9 L）            BS EN ISO  14343-B-SS308L                JIS Z3321 Y308L 0.024 1.72 0.48 ### 0.018 #### 9.83 0.007 0.09 — — 560 45 — 98%Ar+2%O2 Suitable for extra-low carbon 00Cr19Ni10 structures. Also it could fabricat 0Cr18Ni10Ti structures, which working temperature lower than 300℃. E.g. synthetic fibre, fertilizer & chemical industrial equipment and so on.
CHM-308LG AWS A5.9 ER308LSi                                     BS EN ISO  14343-A-G（19 9 L Si）            BS EN ISO  14343-B-SS308LSi   0.020 1.89 0.75 ### 0.010 #### 9.75 0.006 0.15 — 415 605 41  -40℃   81 Ar+1-5%CO2 Specially for railway locomotives, coachs, wagons, vehicles made by atmospheric corrosion and infection resistance steels.
CHM-308LSi AWS A5.9 ER308LSi                                     BS EN ISO  14343-A-G（19 9 L Si）            BS EN ISO  14343-B-SS308LSi   0.021 1.77 0.79 ### 0.018 #### 9.85 0.005 0.17 — — 575 43 — 98%Ar+2%O2 Suitable for extra-low carbon 00Cr19Ni10 stainless steels structures, which need better resistance to inter-crystal corrosion, e.g. synthetic fibre, petrochemical chemical industrial equipments.
CHM-309 AWS A5.9 ER309                                   BS EN ISO  14343-A-G（22 12 H）            BS EN ISO  14343-B-SS309                       JIS Z3321 Y309 0.06 2.05 0.40 ### 0.020 #### 13.26 0.007 0.06 — — 580 39 — 98%Ar+2%O2 Suitable for welding similar chemical composition stainless steel structures and dissimilar steel, e.g. Cr19Ni10 with mild steel, as well as for welding high Mn and High Cr steels.
CHM-309L AWS A5.9 ER309L                                 BS EN ISO  14343-A-G（23 12 L）      BS EN ISO  14343-B-SS309L            JIS Z3321 Y309L 0.026 2.11 0.38 ### 0.017 #### 12.30 0.006 0.15 — — 570 38 — 98%Ar+2%O2 For welding extra low carbon stainless steel structures with sililar chemical composition, such as synthetic fibre, petrochemical equipment as well as nuclear reactor. Also it could be used for dissimilar steel welding.
CHM-309LG AWS A5.9 ER309LSi                               BS EN ISO  14343-A-G（23 12 L Si）            BS EN ISO  14343-B-SS309LSi   0.017 1.93 0.68 ### 0.020 #### 12.40 0.005 0.16 — 415 580 39  -40℃   90  Ar+1-5%CO2 Specially for railway locomotives, coachs, wagons, vehicles made by atmospheric corrosion and infection resistance steels.
CHM-309LSi AWS A5.9 ER309LSi                               BS EN ISO  14343-A-G（23 12 L Si）            BS EN ISO  14343-B-SS309LSi   0.024 2.11 0.68 ### 0.015 #### 12.31 0.004 0.16 — — 560 40 — 98%Ar+2%O2 For welding extra low carbon 00Cr22Ni12 stainless steel structures, such as synthetic fibre, petrochemical equipment as well as nuclear reactor. Also it could be used for dissimilar steel welding.
CHM-310 AWS A5.9 ER310                                  BS EN ISO  14343-A-G（25 20）                  BS EN ISO  14343-B-SS310                         JIS Z3321 Y310 0.09 1.65 0.53 ### 0.014 #### 21.40 0.006 0.18 — — 605 37 — 98%Ar+2%O2 For welding Cr25Ni20 stainless steels structures, which provide good oxidation corrosion resistance and heat resistance. Also it could be used for dissimilar steel welding and for welding high Cr, high Mn steels.
CHM-316 AWS A5.9 ER316                               BS EN ISO  14343-B-SS316                 JIS Z3321 Y316 0.052 2.08 0.52 ### 0.019 #### 11.30 2.18 0.09 — — 580 33 — 98%Ar+2%O2 Mainly for welding structures in chemical industry and power engineering that made by Cr19Ni12Mo2 stainless steels such as AISI316,SUS316. Also it could be used for structures made by high Cr steel and dissimilar steels, which do not need to PWHT.
CHM-316L AWS A5.9 ER316L                              BS EN ISO  14343-A-G（19 12 3 L）               BS EN ISO  14343-B-SS316L                           JIS Z3321 Y316L 0.025 2.05 0.48 ### 0.018 #### 11.50 2.18 0.07 — — 570 34 — 98%Ar+2%O2 Mainly for welding structures in chemical industry and power engineering that made by 00Cr19Ni12Mo2 stainless steels such as AISI316L,SUS316L. Also it could be used for structures made by high Cr steel and dissimilar steels, which do not need to PWHT.
CHM-316LSi AWS A5.9 ER316LSi                            BS EN ISO  14343-A-G（19 12 3 L Si）               BS EN ISO  14343-B-SS316LSi 0.025 2.10 0.85 ### 0.015 #### 11.50 2.18 0.070 — — 580 35 — 98%Ar+2%O2 Suitable for welding extra-low carbon 00Cr19Ni12Mo2 austenitic stainless steel structures and it shows a excellent corrosion resistance. Mainly for chemical industrial equipments.
CHM-321 AWS A5.9 ER321                                   BS EN ISO  14343-B-SS321                     JIS Z3321 Y321 0.028 1.85 0.45 ### 0.019 #### 9.25 0.007 0.07 Ti  0.34 — 575 40 — 98%Ar+2%O2 It is suitable for welding structures made by 1Cr18Ni9Ti austenitic stainless steel as well as the one with similar composition.
CHM-347 AWS A5.9 ER347                                    BS EN ISO  14343-A-G（19 9 Nb）                     BS EN ISO  14343-B-SS347                            JIS Z3321 Y347 0.52 1.81 0.51 ### 0.021 #### 10.01 0.006 0.10 Nb0.59 — 585 39 — 98%Ar+2%O2 It is suitable for welding structures made by 1Cr18Ni11Nb austenitic stainless steel as well as the one with similar composition.
CHM-409 AWS A5.9 ER409                                                          BS EN ISO  14343-B-SS409 0.034 0.29 0.23 ### 0.021 #### 0.26 0.04 0.061 Ti  0.06 — — — — 97%Ar+3%O2 Particularly for welding thin sheet in exhaust system of automobile. 
CHM-410 AWS A5.9 ER410                                                                 BS EN ISO  14343-A-G（13）                         BS EN ISO  14343-B-SS410                          JIS Z3321 Y410   0.06 0.47 0.38 ### 0.011 #### 0.20 0.03 0.17 — — 540 35 — 98%Ar+2%O2 Suitable for welding Cr13 stainless steels. 
CHM-410NiMo AWS A5.9 ER410NiMo                            BS EN ISO  14343-A-G 13 4                             BS EN ISO  14343-B-SS（410NiMo） 0.013 0.66 0.50 ### 0.011 #### 4.79 0.630 0.021 — 735 850 17.5  0℃   80  98%Ar+2%O2 Mainly for welding structures made by martensitic stainless steels, such as 0Cr13Ni5Mo, 15Cr13, 08Cr13 and 08Cr13Al, e.g. the rotating wheel of hydraulic turbine, valves or pumps.  
CHM-NiCrMo-6 AWS A5.14 ERNiCrMo-6                               JIS Z3334 YNiCrMo-6 0.006 2.60 0.37 ### 0.015 #### Balance 5.80 Cu 0.07    Nb  1.08 Fe  1.46     W  1.33 410 675 37  -196℃   150  Ar+30%He+0.5%CO2 Mainly for welding Nickel base alloys. Also it could be used for problem alloys, copious cooling steels and dissimilar metals.